Flexural strength, also known as modulus of rupture, bend strength, or fracture strength, a mechanical parameter for brittle material, is defined as a material's ability to resist deformation under load. The transverse bending test is most frequently employed, in which a rod specimen having either a circular or rectangular cross-section is bent until fracture using a three point flexural test

Three point flexural test

The three point bending flexural test provides values for the modulus of elasticityin bending E_f, flexural stress \sigma_f, flexural strain \epsilon_f and the flexural stress-strain response of the material. The main advantage of a three point flexural test is the ease of the specimen preparation...

 technique. The flexural strength represents the highest stress experienced within the material at its moment of rupture. It is measured in terms of stress, here given the symbol .

Introduction

When an object formed of a single material, like a wooden beam or a steel rod, is bent (Fig. 1), it experiences a range of stresses across its depth (Fig. 2). At the edge of the object on the inside of the bend (concave face) the stress will be at its maximum compressive stress value. At the outside of the bend (convex face) the stress will be at its maximum tensile value. These inner and outer edges of the beam or rod are known as the 'extreme fibers'. Most materials fail under tensile stress before they fail under compressive stress, so the maximum tensile stress value that can be sustained before the beam or rod fails is its flexural strength.

Flexural versus tensile strength

The flexural strength would be the same as the tensile strength

Tensile strength

Ultimate tensile strength , often shortened to tensile strength or ultimate strength, is the maximum stress that a material can withstand while being stretched or pulled before necking, which is when the specimen's cross-section starts to significantly contract...

 if the material was homogeneous. In fact, most materials have small or large defects in them which act to concentrate the stresses locally, effectively causing a localized weakness. When a material is bent only the extreme fibers are at the largest stress so, if those fibers are free from defects, the flexural strength will be controlled by the strength of those intact 'fibers'. However, if the same material was subjected to only tensile forces then all the fibers in the material are at the same stress and failure will initiate when the weakest fiber reaches its limiting tensile stress. Therefore it is common for flexural strengths to be higher than tensile strengths for the same material. Conversely, a homogeneous material with defects only on it surfaces (e.g. due to scratches) might have a higher tensile strength than flexural strength.

If we don't take into account defects of any kind, it is clear that the material will fail under a bending force which is smaller than the corresponding tensile force. Both of these forces will induce the same failure stress, whose value depends on the strength of the material.

For a rectangular sample, the resulting stress under an axial force is given by the following formula : . This stress is not the true stress, since the cross section of the sample is considered to be invariable (engineering stress).

• is the axial load (force) at the fracture point
• b is width
• d is thickness

The resulting stress for a rectangular sample under a load in a three-point bending setup (Fig. 3) is given by the formula below (see "Measuring flexural strength").

The equation of these two stresses (failure) yields :

Usually, L (length of the support span) is much bigger than d, so the fraction is bigger than one.

Measuring flexural strength

For a rectangular sample under a load in a three-point bending setup (Fig. 3):

• F is the load (force) at the fracture point
• L is the length of the support span
• b is width
• d is thickness

For a rectangular sample under a load in a four-point bending setup where the loading span is one-third of the support span:

• F is the load (force) at the fracture point
• L is the length of the support (outer) span
• b is width
• d is thickness

For the 4 pt bend setup, if the loading span is 1/2 of the support span (i.e. L_i = 1/2 L in Fig. 4):


If the loading span is neither 1/3 or 1/2 the support span for the 4 pt bend setup (Fig. 4):

• L_i is the length of the loading (inner) span